Die casting method
Slush casting method
Permanent mould casting method
Centrifugal casting method
C. Permanent mould casting method
Aluminium
Wax
Lead
All of these
1 to 5 volts
6 to 10 volts
11 to 20 volts
50 to 100 volts
Smoothing and cleaning out depressions in the mould
Cleaning the moulding sand
Moistening the sand around the edge before removing pattern
Reinforcement of sand in the top part of the moulding box
30% sand and 70% clay
50% sand and 50% clay
70% sand and 30% clay
90% sand and 10% clay
+0.05 mm
±0.2 mm
+0.5 mm
±1 mm
One side of the actual size
One side of the nominal size
Both sides of the actual size
Both sides of the nominal size
For finishing flat surfaces
For necking down a piece of work
For punching a hole
To finish the punched hole
Zinc chloride
Ammonium chloride
Rosin plus alcohol
Borax
TIG welding
MIG welding
Manual arc welding
Submerged arc welding
Same as
Less than
More than
None of these
Increasing the cross-section of a bar
Reducing the cross-section of a bar
Joining the two surfaces of metal under pressure after heating
Bending of a bar
Camber on the rolls
Offset on the rolls
Hardening of the rolls
Antifriction bearings
Neutral flame and rightward technique
Oxidising flame and leftward technique
Neutral flame and leftward technique
Carburising flame and rightward technique
Continuous spot welding process
Multi-spot welding process
Arc welding process
Process used for joining round bars
Actual deviation
Upper deviation
Lower deviation
Fundamental deviation
Work is connected to the positive terminal and the electrode holder to the negative terminal
Work is connected to the negative terminal and the electrode holder to the positive terminal
Work is connected to the positive terminal and the electrode holder is earthed
Work is connected to the negative terminal and the electrode holder is earthed
Compressive stress in the flange
Tensile stress in the wall
Both (A) and (B)
None of these
Porosity of the metal is largely eliminated
Grain structure of the metal is refined
Mechanical properties are improved due to refinement of grains
All of the above
Flat chisel
Cape chisel
Round nose chisel
Diamond pointed chisel
It evolves a great amount of steam and other gases
The sand grains stick together
It clings to the sides of a moulding box
None of these
Cold shuts
Blow holes
Shift
Swell
5 cm × 5 cm
10 cm × 10 cm
15 cm × 15 cm
20 cm × 20 cm
Carbon arc welding
Submerged arc welding
TIG arc welding
MIG arc welding
Deliver molten metal into the mould cavity
Act as a reservoir for the molten metal
Feed the molten metal to the casting in order to compensate for the shrinkage
Deliver the molten metal from pouring basin to gate
The angular clearance on dies varies from 0.5° to 1°
In drawing operation, the metal flows due to plasticity
In press operation, the size of the pierced hole is independent of the size of punch
None of the above
8
12
18
20
One is working roll and three are backing up rolls
Two are working rolls and two are backing up rolls
Three are working rolls and one is backing up roll
All of the four are working rolls
Ram the sand harder at the pattern face with decreasing hardness towards the back of the mould
Ram the sand harder at the back of the mould and softer on the pattern face
Produce uniform packing of sand in the mould
Give uniform sand hardness throughout the mould
Sand slinger
Squeezing machine
Jolt machine
Stripper plate machine
Age hardening
Work hardening
Induction hardening
Flame hardening