Cast iron
Wrought iron
Steel
All the above
D. All the above
Slump is 50 to 75 mm
Flexural strength at 90 days is 0.2 N/mm2
Compressive strength at 90 days is 1.5 N/mm2
All the above
Acid test is done to find out the weathering quality of stones
Attrition test is done to find out the rate of wear of stones which are used in road construction
Crushing test is done to find out the compressive strength of the stone
All the above
Sandy clay, calcareous clay, pure clay
Calcareous clay, pure clay, sandy clay
Pure clay, sandy clay, calcareous clay
None of these
Rust is due to formation of oxides
Cast iron oxidises less
Steel oxidises most
All the above
Sedimentary rocks
Metamorphic rocks
Igneous rocks
All the above
Split easily
Are affected by moisture
Both (A) and (B)
None of these
Strength
Rigidity
Elasticity
All of these
Alcohol
Linseed
Turpentine
All the above
Cast steel
Bessemer steel
Mild steel
Whitworth compressed steel
The average crushing strength of hand moulded bricks is 6000 t/m2
The average tensile strength of hand moulded brick is 200 t/m2
The average shearing strength of hand moulded brick is 600 t/m2
All the above
Be durable
Be free from clay
Resist action of acids
All the above
To make it water proof
To paint its surface
To increase its temperature
To remove water
Larger proportion of lime grounded finer than normal cement
Lesser proportion of lime grounded coarser than normal cement
Lesser proportion of lime grounded finer than normal cement
Excess percentage of gypsum
Shale powder
Talc powder
Asbestos powder
Plastic powder
Sedimentary rock
Metamorphic rock
Igneous rock
Volcanic rock
Sedimentary rock
Stratified rock
Aqueous rock
Metamorphic rock
For thin structures subjected to wetting and drying, the water cement ratio should be 0.45
For mass concrete structures subjected to wetting and drying, the water ratio should be 0.55
For thin structures which remain continuously under water, the watercement ratio by weight should be 0.55
All the above
190 mm × 90 mm × 80 mm
190 mm × 190 mm × 90 mm
200 mm × 100 mm × 100 mm
200 mm × 200 mm × 100 mm
Cast iron
Wrought iron
Steel
All the above
12% of nickel
24% of nickel
30% to nickel
36% of nickel
Queen closer
King closer
Closer
Squint brick
Intrusive igneous rock
Extrusive igneous rock
Sedimentary rock
Metamorphic rock
Cellulose acetate plastics
Polyvinyl chloride plastics
Phenol formaldehyde plastic
Urea formaldehyde plastic
Slate
Plank
Board
Strip
30 minutes
1 hour
6 hours
10 hours
Along the direction of bedding planes
At 45° to the direction of bedding planes
At 60° to the direction of bedding planes
Perpendicular to the direction of bedding planes
Lime stone and alumina
Silica and alkalies
Alumina and iron
Alkalies and magnesium
Carbon
Sulphur
Vanadium
Chromium
Is used as water proofing material
Is used as damp proofing material
Is made from bitumen and hessian fibres
All the above
Tri-calcium silicate
Di-calcium silicate
Tri-calcium aluminate
Tetra calcium alumino ferrite