Related Questions
What is the correct answer?
4
While the recrystallisation temperature for pure metals is 0.3 Tm, the same for alloys is equal to __________ × Tm (where, Tm Melting temperature).
What is the correct answer?
4
Diameter of the rivet to be provided on a 20 mm. thick boiler plate will be __________ mm.
What is the correct answer?
4
The excess air required for the combustion of pulverised coal is of the order of about __________ percent.
What is the correct answer?
4
Which of the following forces does not act on a fluid at rest?
What is the correct answer?
4
Maximum change in the hardness of martensite occurs in the carbon content range of __________ percent in steel.
What is the correct answer?
4
An ideal material for making cooking vessels should have
C. High thermal conductivity
What is the correct answer?
4
__________ of air does not increase with increase in temperature.
What is the correct answer?
4
The approximate height of a blast furnace having a useful volume of 2000 m3 is about __________ metres
What is the correct answer?
4
The temperature at which ferromagnetic material can no longer be magnetised by the outside forces, is termed as the
What is the correct answer?
4
The main constituent of bones is
What is the correct answer?
4
Which of the following has the highest value of refractive index?
What is the correct answer?
4
Which of the following is an ore dressing operation?
What is the correct answer?
4
Melting point & boiling points of liquid oxygen are respectively - 218.8°C & - 183°C, while the same for liquid nitrogen is - 210°C & - 195.8°C respectively. The difference in melting points of liquid oxygen & liquid nitrogen is not equal to 8.8
What is the correct answer?
4
With increase in impurities in metals, their corrosion resistances
D. May increase or decrease; depending on the type of metal
What is the correct answer?
4
The product out from a cupola is called
What is the correct answer?
4
Broaching tools are usually made of
What is the correct answer?
4
The cathode in an electrochemical cell always carries
D. Positive or negative charge depending upon the nature of the cell
What is the correct answer?
4
The diffusion co-efficient of Ni in Cu at 1000 K is 1.93 × 10-16 m2S-1 and it is 1.94 × 10-14 m2S- 1 at 1200 K. The activation energy (in k. J.mole-1) for the diffusion of Ni in Cu is
What is the correct answer?
4
The __________ of a double acting reciprocating pump as compared to the single acting pump will be almost double.
What is the correct answer?
4
Lead is poured into the joint between two- __________ pipes.
What is the correct answer?
4
Silicon in steel
A. Makes it usable in almost all magnetic circuits where alternating current is used
B. Increases its electrical resistivity and decreases the hysteresis loss
C. Is present upto 5% & 4% respectively when used in transformers & motor armatures
What is the correct answer?
4
The leaching solvent used in Baeyer's process for the purification of bauxite is
What is the correct answer?
4
Heating the Hypo-eutectoid steels to 30°C above the upper critical temperature line, soaking at that temperature and then cooling slowly to the room temperature to form a pearlite & ferrite structure is called
What is the correct answer?
4
Minimum temperature upto which water can be theoretically cooled down in the cooling tower by evaporative cooling is equal to the __________ temperature of air.
What is the correct answer?
4
Shaft/rotor speed is most accurately measured by a
What is the correct answer?
4
Projection welding & stud welding is categorised as the __________ welding.
What is the correct answer?
4
A metal having a Poisson's ratio = 0.3 is elastically deformed under uniaxial tension. If the longitudinal strain = 0.8, then the magnitude of thickness strain is
What is the correct answer?
4
The noble metals
A. Are exemplified by Na, K and Li
B. Do not resist corrosion very strongly
C. Are the lowermost in the electro-chemical series of metals
What is the correct answer?
4
A reduction in thermal resistance during heat transfer does not occur in the
A. Convection heat transfer by stirring the fluid and cleaning the heating surface
B. Conduction heat transfer by reduction in the material thickness and increase in the thermal conductivity
C. Radiation heat transfer by increasing the temperature and reducing the emissivity
What is the correct answer?
4
Powder metallurgy is used to produce
A. High precision components with complex cavities and sharp features
B. Components of large size
C. Porosity free components
D. Components of such alloys whose constituents do not form alloys readily